PA66 AKV 30 G H2.0 SR1 900051德國朗盛Durethan 30%玻纖熱老化穩(wěn)定尼龍66塑料（18024445500）

PA 66, 30 % glass fibers, injection molding, heat-aging stabilized, improved surface finish



ISO Shortname: ISO 1874-PA 66, GHR, 14-100, GF30

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 280 °C / MT 80 °C; 500 bar % acc. ISO 2577 0.25　
Molding shrinkage, transverse 150x105x3; 280 °C / MT 80 °C; 500 bar % acc. ISO 2577 0.94　
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.04　
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.08　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 9600 6500
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 180 120
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 6.0
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 70 75
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 60 60
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 10 15
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA < 10 < 10
Charpy notched impact strength -40 °C kJ/m² ISO 179-1eA < 10 < 10
Izod impact strength 23 °C kJ/m² ISO 180-1U 55 65
Izod impact strength -30 °C kJ/m² ISO 180-1U 50 50
Izod notched impact strength 23 °C kJ/m² ISO 180-1A < 10 < 10
Izod notched impact strength -30 °C kJ/m² ISO 180-1A < 10 < 10
Flexural modulus 2 mm/min MPa ISO 178-A 8400 5600
Flexural strength 2 mm/min MPa ISO 178-A 270 170
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.0 6.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 260 150
C Puncture maximum force 23 °C N ISO 6603-2 740 920